Stainless Steel Welding Rod RNY309Mo
Codice componente
Qui sono indicati i codici componente
correlati al prodotto ricercato
Informazioni di base
| Product Type | Barra per saldatura | Pole diameter(mm) | 4 | Pole length(mm) | 350 |
|---|---|---|---|---|---|
| Current range, lower(A) | 110～150 | Current range, vertical position, elevating, upper | 85～135 | JIS Standard | ES309Mo-16 Equivalent |
| AWS Standard | E309Mo-16 Equivalent | Mechanical property: Tensile strength(MPa) | 650 (example, JIS standard: 550:≤) | Mechanical property: 5D elongation(%) | 37.4 (example, JIS standard: 25:≤) |
| Mechanical property: Absorbed energy(J) | 82（20℃） | Identification Color | End Surface: Silver, Side Surface: - | Amount Of Content | 1 Box (5 kg) |
| Applications and Special Features | While used for application similar to RNY309, its corrosion-resistance under normal temperature is equivalent to RYN316, and crack-resistance is further superior by adding Mo. Preferred to be used for welding stainless clad steel and curing alloy steel for usage under normal temperature. Coating of lime titania type allows welding in any posture. | Ferrite Quantity: (method) Schaeffler Diagram(%) | 15.0 | Notes | Please dry at 150–200°C for approximately 1 hour prior to use. When welding, remove all oil, dust and other foreign material from the welding surface. |
Configura
Proprietà di base
-
Tipo
- RNY309MO
Filtrare per giorni di spedizione standard
-
- Tutti gli articoli
- 9 giorni o meno
Attributi opzionali
- Specifiche e dimensioni di alcuni componenti potrebbero non essere illustrate in modo esauriente. Per i dettagli esatti, consultare i cataloghi dei produttori .
Supporto tecnico
Metodo di pagamento
Produzione on demand
Certificati
Copyright © MISUMI Corporation All Rights Reserved.