WEICON VA 30 Black
Fare clic sull'immagine per ingrandirla.
Cliccare sull´immagine per ingrandirla.
Cyanoacrylate Adhesive for special requirements, rubber-filled, high temperature resistant, medium viscosity, longer curing, residual elasticity after curing, high peel and impact resistance
WEICON Contact VA 30 Black has medium viscosity (300 mPa•s) and is temperature resistant between -50°C (-58°F) and +135°C (+275°F). It has a longer curing time, is rubber-filled and black, hardens with residual elasticity and has high peel and impact strength. Thanks to its curing with residual elasticity, WEICON Contact VA 30 Black is particularly suitable under changing climatic conditions. It is insensitive even under a longer influence of humidity.
VA 30 Black is ideally suited for the bonding of diverse rubber materials such as solid rubber or cellular rubber, plastics and metal/plastic joints.
WEICON Contact VA 30 Black has medium viscosity (300 mPa•s) and is temperature resistant between -50°C (-58°F) and +135°C (+275°F). It has a longer curing time, is rubber-filled and black, hardens with residual elasticity and has high peel and impact strength. Thanks to its curing with residual elasticity, WEICON Contact VA 30 Black is particularly suitable under changing climatic conditions. It is insensitive even under a longer influence of humidity.
VA 30 Black is ideally suited for the bonding of diverse rubber materials such as solid rubber or cellular rubber, plastics and metal/plastic joints.
Codice componente
Qui sono indicati i codici componente
correlati al prodotto ricercato
Loading...
Configura
Proprietà di base
-
Tipo
- 12603012
- 12603030
- 12603060
- 12603500
Filtrare per giorni di spedizione standard
-
- Tutti gli articoli
- 3 giorni o meno
Attributi opzionali
- Specifiche e dimensioni di alcuni componenti potrebbero non essere illustrate in modo esauriente. Per i dettagli esatti, consultare i cataloghi dei produttori .
Supporto tecnico
Metodo di pagamento
Produzione on demand
Certificati
Copyright © MISUMI Corporation All Rights Reserved.